Material:Fiberglass, cotton, Fiberglass+PTFE, Basalt, silica woven cloth
DESCRIPTION:
1.Fiberglass Woven filter cloth
Type:
(1) Flat fiberglass filter cloth
(2) Textured fiberglass filter cloth
Features: Fiberglass filter cloth has high covering capacity and good air permeability, thus providing higher filtration efficiency,lower filtration resistance.
Application:
Pipe Insulation–High Temperature resistence.
High Temperature Insulation–High Temperature resistence.
Insulation Enhancement–Our products can be used in the field of insulation enhancement.
Insulation Rubber Tape–Insulated rubber tape specifically refers to the tape used by electricians to prevent leakage and to provide insulation.
Screen Cloth–Our products can be used to make screen cloth.
Aviation Material–Aviation materials are the material guarantee for the development and production of aerospace products, and also the technical foundation for the aerospace products to achieve the desired performance, service life and reliability. It is very reliable to use our fiberglass filter cloth for aviation material.
Film Material–The core of membrane technology is membranes. In general, the chemical properties and structure of the membrane have a decisive influence on the properties of the membrane separation. Therefore, it is required that the membrane material should have good film forming properties, chemical stability, resistance to acids, alkalis, oxides, and microorganisms.
PTFE High Frequency Substrate–Fiberglass filter cloth is widely used in PTFE high frequency substrate.
2.Basalt filter cloth
Features: Basalt filter cloth not only has a perfect performance in resisting high temperature,but also can be degraded totally. It is a eco-friendly industrial material.
Performance:
(1) It can resist strong alkali and acid except chlorine-sulphur acid and thick nitric acid.
(2) The general temperature applied is less 650℃,the tensility will fall off and shrink
Applications details
Cement Plant | |||||||
Product Specification sheets | |||||||
Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition | Tensile Strength（N/25mm） | Running Temperature | |
Warp | Weft | ||||||
PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
Steel Plant | |||||||
Product Specification sheets | |||||||
Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition | Tensile Strength（N/25mm） | Running Temperature | |
Warp | Weft | ||||||
PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
Graphite Finished + Membrane | 2/5 Satin | 550±15 | 2—5 | >3 | >2000 | >2000 | ≦260 |
Graphite Finished + Membrane | 2/5 Satin | 550±15 | 30—50 | >1.5 | >2000 | >2000 | ≦260 |
Coal-fired Boiler | |||||||
Product Specification sheets | |||||||
Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition | Tensile Strength | Running Temperature | |
Warp | Weft | ||||||
Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
Ferroalloys | |||||||
Product Specification sheets | |||||||
Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition | Tensile Strength（N/25mm） | Running Temperature | |
Warp | Weft | ||||||
Acid-Resistant Finished + Membrane | 1/3 Twill | 500±15 | 2—5 | >10 | >2000 | >1200 | ≦260 |
Acid-Resistant Finished + Membrane | 1/3 Twill | 340±15 | 2—5 | >10 | >1300 | >800 | ≦260 |
Graphite Finished + Membrane | 2/5 Satin | 550±15 | 2—5 | >3 | >2000 | >2000 | ≦260 |
Graphite Finished + Membrane | 2/5 Satin | 550±15 | 30—50 | >1.5 | >2000 | >2000 | ≦260 |
Biomass Power Generation | |||||||
Product Specification sheets | |||||||
Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition | Tensile Strength（N/25mm） | Running Temperature | |
Warp | Weft | ||||||
PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
Acid-Resistant Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
Chemical Plants | |||||||
Product Specification sheets | |||||||
Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition | Tensile Strength | Running Temperature | |
Warp | Weft | ||||||
PTFE Finished + Membrane | Double Twill | 750±25 | 2—5 | >10 | >2400 | >2000 | ≦260 |
Carbon Black | |||||||
Product Specification sheets | |||||||
Finish | Weave Pattern | Weight（g/m2） | Air Permeability（cm3/cm2·s@127pa） | Loss on lgnition | Tensile Strength（N/25mm） | Running Temperature | |
Warp | Weft | ||||||
PTFE Graphite Silicone Finished | 1/3 Twill | 470±15 | 15—30 | >3 | >2000 | >1000 | ≦260 |
Acid-Resistant Finished + Membrane | 1/3 Twill | 500±15 | 2—5 | >10 | >2000 | >1200 | ≦260 |